Good Quality Welding Flux for Saw Wire
| Reference FOB Price: | US $400.00 / Ton |
|---|---|
| Min. Order: | 5 Tons |
| state: | Solid |
|---|---|
| pH: | Alkaline |
| Type: | Inorganic |
Basic Info
Model NO.
SJ101
Melting Point
>600℃
Chemical Composition
MnO=15%-30%
Function
Protect Weld Metal
Application
Submerged-arc Welding
Manufacturing Method
Non-melting
Mesh Size:10-60 Mesh
Package:25kg/Kraft Paper Bag;1000kg/Jumbo Bag
Transport Package
25kg/Kraft Paper Bag; 1000kg/Jumbo Bag
Specification
size: 10-60 Mesh
Trademark
QILU BRAND
Origin
Shangdong
HS Code
38109000
Production Capacity
20000 Mt/Year
Product Description
Flux SJ101 Agglomerated Flux for S. A. Welding
GB/T12470-2003 F48A4-H10Mn2
AWS A5.23 F7A4-EH14
Flux SJ101 is a type of fluorine and alkali based agglomerated flux, the basicity of which is about 1.8, gray spherical grains in appearance. Its grain size is 2.0-0.28mm (10-60 meshes). Peony Flux SJ101 is suitable for use with AC or DC power; filler wires connect with Positive Electrode while in DC, the maximum current can reach to 1200 amps. With stable burning arc, the flux provides very good weld bead appearance and excellent slag removal. Additional Feathers are good performance of low temperature impact toughness towards weld bead metals.
Combined with appropriate SAW wires such as H08MnA, H08MnMoA, H08Mn2MoA, H10Mn2, the flux is capable of welding multiple important low alloy steel structures, like boilers, pressure vessels, and pipelines. Flux SJ101 can also be applied to multi-wire submerged arc welding, especially in double-side single pass welding of large diameter containers.
Mechanical Properties of Deposited Metal
Packaging
Remarks
1. Redry the flux at 300~350ºC for 2 hours before welding.
2. Impurities such as rust, greasy dirt, moisture, etc. should be cleared from welding area.
GB/T12470-2003 F48A4-H10Mn2
AWS A5.23 F7A4-EH14
Flux SJ101 is a type of fluorine and alkali based agglomerated flux, the basicity of which is about 1.8, gray spherical grains in appearance. Its grain size is 2.0-0.28mm (10-60 meshes). Peony Flux SJ101 is suitable for use with AC or DC power; filler wires connect with Positive Electrode while in DC, the maximum current can reach to 1200 amps. With stable burning arc, the flux provides very good weld bead appearance and excellent slag removal. Additional Feathers are good performance of low temperature impact toughness towards weld bead metals.
Combined with appropriate SAW wires such as H08MnA, H08MnMoA, H08Mn2MoA, H10Mn2, the flux is capable of welding multiple important low alloy steel structures, like boilers, pressure vessels, and pipelines. Flux SJ101 can also be applied to multi-wire submerged arc welding, especially in double-side single pass welding of large diameter containers.
Mechanical Properties of Deposited Metal
| Wire | Tensile Strength R m (MPa) | Yield Strength R eh (MPa) | Elongation A % | AKV(J) | ||
| 0ºC | -20ºC | -40ºC | ||||
| H08MnA | 450~550 | ≥360 | ≥24 | ≥110 | ≥80 | ≥34 |
| H10Mn2 | 480~650 | ≥400 | ≥24 | ≥110 | ≥80 | ≥34 |
| H08MnMoA | 550~650 | ≥430 | ≥24 | ≥70 | ≥34 | |
| H08Mn2MoA | 620~750 | ≥500 | ≥24 | ≥70 | ≥34 | |
| Unit | bags | Net Weight | 25Kg |
1. Redry the flux at 300~350ºC for 2 hours before welding.
2. Impurities such as rust, greasy dirt, moisture, etc. should be cleared from welding area.