Welding Flux Saw Submerged Arc Flux Sj101 Sj301 Sj501
Purchase Qty.: (Tons) |
1-9 10+ |
---|---|
Reference FOB Unit Price: | US $600.00 US $500.00 |
state: | Solid |
---|---|
pH: | Alkaline |
Type: | Inorganic |
Melting Point: | >600℃ |
Chemical Composition: | MnO=15%-30% |
Function: | Protect Weld Metal |
Basic Info
Model NO.
welding flux SJ301, SJ101, SJ501
Application
Submerged-arc Welding
Manufacturing Method
Non-melting
Model No.
Welding Flux Sj501
Sample
Can Offered
Certification
ABS,CCS,Lr,BV
Quality System
ISO9001: 2000
Performance
Easy to Slag, Smooth Welding Bead
Content
Fluorine, Alkali
Port
Qingdao
Color
Grey
Current
AC or DC
Grain Size
2.0-0.45mm (10-40 Mesh)
Transport Package
25 Kg/Kraft Paper Bag, 40 Bags/Pallet
Specification
ABS, CCS, LR
Trademark
QILU Brand
Origin
Zibo, Shandong, China
HS Code
3801900000
Production Capacity
100000mt/Year
Product Description
In Accordance With: NB/T47018-2011 GB/T5293-1999 F5AZ-H08A F5A2H08MnA
AWS-A5.17 F7AZ-EL12 F7A2-EM12K
Welding flux is needed while submerged arc wire welding.
There are SJ101, SJ301 and SJ501 in our warehouse.
Description:
Agglomerated flux SJ501 is a kind of acid aluminum-titanium type sintered flux, the basicity index is
about 0.8. It is shaped as black, round grains and its grain size is 2.0-0.28mm (10-60Mesh). It can be
used with either AC or DC. The welding wire is connected to the positive electrode when used with DC. It
has stable combustion, good slag detachability and good appearance of weld. It has a thick skin to
a small quality of rust and high temperature oxidation film on account of strong the capability of resist
pore.
As a peculiar production technique is adopted, the flux possesses better moisture resistance and good
strength of grains, which may satisfy the requirements for regular transportation, storage and recycling
use in welding. The flux has less specific gravity when it is bulk packed. And it is consumed less during
the welding.
Usage:
1. for low carbon, low alloy and pipeline steel.
2. for thick wall structures of different high-tensile steels.
Cautions:
1.The oil contamination, moisture, iron rust and other foreign substances must be removed from the
welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 300-350°C for more than 2 hours before usage.
Chemical Compositions:
Notes for welding:
1. Redry the flux for 2 hours at 300-350º C prior to be used.
2. Some rust, oil, moisture and other impurities must be cleared away from the area to be welded.
Application:
With suitable welding wires(H08MnA. H08MnMoA. H10Mn2), it can welding common structural steel, boiler
steel, pipeline steel, etc. The flux can be used for multiple fast welding, and can be suitable for single-
sided welding, especially suitable for pressure vessel, such as oil and gas pipes, tanks and cylinders of
automatic submerged arc welding.
(Mechanical Performance of the Deposited Metal):
Mechanical Property:(according to GB5293-1999 F4A1-H08A)
Our Service:
1. Professional service for products
2. Much more competitive price
3. Honest and excellent supplier
4. Delivery time is shorter than others.
5. We believe the good quality is the basis for cooperation.
6. We could provide the samples for test to you.
7. Our company policy is Quality First, and to establish Long Time business, not just one time
How to contact us?
Mr. Jacky-MIGHTY QINGDAO METAL MATERIALS CO., LTD.
Tel: +86-0532-66010296
Mobile: +86-15764260250
Add: Room 705, Building A, Heda Office Building, NO. 175, Tailiu Road, Shibei Strict, Qingdao, China
AWS-A5.17 F7AZ-EL12 F7A2-EM12K
Welding flux is needed while submerged arc wire welding.
There are SJ101, SJ301 and SJ501 in our warehouse.
Description:
Agglomerated flux SJ501 is a kind of acid aluminum-titanium type sintered flux, the basicity index is
about 0.8. It is shaped as black, round grains and its grain size is 2.0-0.28mm (10-60Mesh). It can be
used with either AC or DC. The welding wire is connected to the positive electrode when used with DC. It
has stable combustion, good slag detachability and good appearance of weld. It has a thick skin to
a small quality of rust and high temperature oxidation film on account of strong the capability of resist
pore.
As a peculiar production technique is adopted, the flux possesses better moisture resistance and good
strength of grains, which may satisfy the requirements for regular transportation, storage and recycling
use in welding. The flux has less specific gravity when it is bulk packed. And it is consumed less during
the welding.
Usage:
1. for low carbon, low alloy and pipeline steel.
2. for thick wall structures of different high-tensile steels.
Cautions:
1.The oil contamination, moisture, iron rust and other foreign substances must be removed from the
welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 300-350°C for more than 2 hours before usage.
Chemical Compositions:
Al2O3+MnO | CaO+MgO | SiO2+TiO2 | CaF2 | S | P |
25~30 | 25~30 | 15~20 | 15~20 | ≤0.03 | ≤0.03 |
Notes for welding:
1. Redry the flux for 2 hours at 300-350º C prior to be used.
2. Some rust, oil, moisture and other impurities must be cleared away from the area to be welded.
Application:
With suitable welding wires(H08MnA. H08MnMoA. H10Mn2), it can welding common structural steel, boiler
steel, pipeline steel, etc. The flux can be used for multiple fast welding, and can be suitable for single-
sided welding, especially suitable for pressure vessel, such as oil and gas pipes, tanks and cylinders of
automatic submerged arc welding.
(Mechanical Performance of the Deposited Metal):
Wires | Standard Models | бs(Mpa) | бb(Mpa) | δ5 | Akv(J) |
HO8A | F4A2-HO8A | ≥330 | ≥420 | ≥22% | ≥27 |
HO8MnA | F5A2-HO8MnA | ≥400 | ≥500 | ≥22% | ≥27 |
Fit | GB/T5293-1999 | F4A2-H08A | F5A2-H08MnA |
Equivalent to | AWS-A5·17 | F6A2-EL12 | F7A3-EM12 |
Mechanical Property:(according to GB5293-1999 F4A1-H08A)
Test Item | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Impact Absorption Rate (J) |
-40οC | ||||
Guaranteed Value | 410~550 | ≥330 | ≥22.0 | ≥27 |
Our Service:
1. Professional service for products
2. Much more competitive price
3. Honest and excellent supplier
4. Delivery time is shorter than others.
5. We believe the good quality is the basis for cooperation.
6. We could provide the samples for test to you.
7. Our company policy is Quality First, and to establish Long Time business, not just one time
How to contact us?
Mr. Jacky-MIGHTY QINGDAO METAL MATERIALS CO., LTD.
Tel: +86-0532-66010296
Mobile: +86-15764260250
Add: Room 705, Building A, Heda Office Building, NO. 175, Tailiu Road, Shibei Strict, Qingdao, China